Title: Mechanical Properties and Microstructural features of Overmolded Polymer Composite Lattice Structures

Authors: Segun Talabi, Ryan Ogle, Brittany Rodriguez, Sana Elyas, Vlastimil Kunc, Ahmed Hassen

DOI: 10.33599/nasampe/s.25.0229

Abstract: This study investigates the mechanical properties and interfacial bonding of Polyamide 12 filled with Glass Fiber (PA12/GF) lattice structures overmolded with Nylon 66 (PA66) and Thermoplastic Polyurethane (TPU). The PA12/GF lattices, designed in Gyroid, Isotruss, and Octahedral geometries, were produced using the Selective Laser Sintering (SLS) technique. The thermal characteristics of both the lattice and overmolding materials were analyzed using Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA). The mechanical performance and interfacial bonding were evaluated through mechanical testing and microstructural analysis. The results indicate that overmolding improved flexural strength and impact resistance of the PA12/GF lattices. For instance, the plain PA12/GF Isotruss lattice exhibited a flexural strength of 15.5 MPa. By overmolding it with TPU the flexural strength increased by up to 137%, while PA66-overmolding resulted in an increase of 371%, achieving a flexural strength of 73 MPa. In terms of impact resistance, TPU-overmolding improved performance significantly, with an increase of 1800% (Gyroid) compared to the plain lattice. Microstructural analysis revealed good adhesion at the interface, especially when both the lattice and overmolding materials were thoroughly dried prior to the overmolding process to minimize interfacial porosity. This study highlights the potential of using overmolding to enhance lattice structures performance, offering lightweight and cost-efficient solutions for automotive applications.

References: [1] Research Nester, Thermoplastic Prepreg Market Size and Share, 2024. [2] N. Larson, et al., Developing a Lab Scale Solvent-Based Prepreg Treater, Western Washington University, 2015. [3] Poly(methyl methacrylate) Sigma Aldrich, wwu.sigmaaldrich.com. https://wwu.sigmaaldrich.cn/CN/product/aldrich/182230. (Accessed Dec. 12, 2023). [4] Nourvon, Perkadox 16 Di(4-tert-butylcyclohexyl) peroxydicarbonate, Nourvon, 2024. [5] Nouryon, Laurox Product Data Sheet, http://www.nouryon.com. (Accessed Jun. 7, 2022). [6] IGM Resins, Omnirad 819 Photoinitiator Product Data Sheet, IMG Resins, 2017. [7] Esstech, PL-032: Bis Acyl Phosphine Technical Data Sheet, Esstech, 2022. [8] Bcomp, ampliTex Technical Data Sheet Ref. 5040, 2024. [9] JPS, 7628 E-glass Fabric Technical Data Sheet, 2024. [10] Mount Vernon Mills, Linen 41 inch QA report, 2024. [11] ASTM E1131, Standard Test Method for Compositional Analysis by Thermogravimetry, 2020. [12] ASTM D2584, Standard Test Method for Ignition Loss of Cured Reinforced Resins, 2018. [13] ASTM D3039/D3039M-17, Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials, 2017. [14] ASTM D2344/D2344M-13, Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates, 2013. [15] ASTM D7264/D7264M-15, Standard Test Method for Flexural Properties of Polymer Matrix Composite Materials, 2015. [16] J. Brandrup, et al. Polymer Handbook, New York, 1998.

Conference: SAMPE 2025

Publication Date: 2025/05/19

SKU: TP25-0000000229

Pages: 17

Price: $34.00