Title: Effect of Fiber-Matrix Co-Carbonization on Carbon-Carbon Composite Pore Morphology

Authors: William Beck, Joseph Stanzione III, James Newell

DOI:

Abstract: Carbon-carbon composites (CCCs) are essential components in aerospace and defense industries because of their unparalleled ability to maintain exceptional thermomechanical properties at extreme temperatures. Widespread application beyond these industries is not economically practical due to the excessive cost and time associated with processing these materials. CCCs predominantly begin as carbon fiber-reinforced polymers (CFRPs) which are pyrolyzed to convert the matrix precursor to a carbon-rich one. As the matrix is pyrolyzed, the inert carbon fibers prevent shrinkage in plane of the fabric which promotes stress-induced cracking within the material. Densification of these cracks is the bottleneck that drives up processing cost and time. It is hypothesized here that CCCs can be produced with advantageous pore morphologies by replacing carbon fibers with polymer fibers that exhibit similar thermomechanical behavior as the matrix during pyrolysis. Previous co-carbonization studies relied on the same fiber–matrix system, characterized by dissimilar thermomechanical behavior during pyrolysis, and did not consider alternative pairings that could better complement each other. In this study, thermomechanical analysis (TMA) was used to characterize poly(p-phenylene-2,6benzobisoxazole) (PBO) fibers, and a benzoxazine-based polymer was selected to match their shrinkage behavior. A PBO fiber–reinforced polymer composite was fabricated via resin transfer molding (RTM), and its thermomechanical behavior was characterized using TMA in both inplane and transverse orientations relative to the fabric. The in-plane response primarily reflects fiber reinforcement, whereas the transverse response is strongly influenced by the polymer matrix. Thermal degradation of PBO generates a larger volume of volatile gases, which enlarges and interconnects cracks, as confirmed by optical microscopy. The resulting pore network exhibits higher permeability, enabling more efficient densification compared to CFRP-based systems. Heat treatment of the fiber has shown that manipulating the fiber shrinkage enables tuning of the pore morphology in CCCs, offering a pathway to more controlled and efficient densification.

References: [1] Fitzer, Erich and Lalit M. Manocha. Carbon Reinforcements and Carbon /Carbon Composites, Springer-Verlag Berlin Heidelberg, 1998. [2] Savage, G. Carbon Carbon Composites, London: Chapman & Hall, 1993. [3] Muhammed, Faheem, Tania Lavaggi, Suresh Advani, Mark Mirotznik and John W. Gillespie. "Influence of Material and Process Parameters on Microstructure Evolution during the Fabrication of Carbon–Carbon Composites: A Review." Journal of Materials Science 56 (2021): 17877-914 [4] [5] [6] [7] [8] Manocha, Lalit M. "High Performance Carbon-Carbon Composites." Sadhana 28 (2003): 349-58 Schulte-Fischedick, J., S. Seiz, N. Lützenburger, A. Wanner and H. Voggenreiter. "The Crack Development on the Micro- and Mesoscopic Scale during the Pyrolysis of Carbon Fibre Reinforced Plastics to Carbon/Carbon Composites." Composites Part A: Applied Science and Manufacturing 38 (2007): 2171-81 Alghamdi, Abdulrahman, Aftab Khan, Paul Mummery and Mohammad Sheikh. "The Characterisation and Modelling of Manufacturing Porosity of a 2-D Carbon/Carbon Composite." Journal of Composite Materials 48 (2014): 2815-29 Sharma, Rajneesh, Vinit V. Deshpande, Atul R. Bhagat, Puneet Mahajan and Ramesh K. Mittal. "X-Ray Tomographical Observations of Cracks and Voids in 3d Carbon/Carbon Composites." Carbon 60 (2013): 335-45 Dhami, TL and OP Bahl. "Challenges in Carbon/Carbon Composites Technologies." Carbon letters 6 (2005): 148-57 [9] Marković, Vesna and Slobodan Marinković. "A Study of Pyrolysis of Phenolic Resin Reinforced with Carbon Fibres and Oxidized Pan Fibres." Carbon 18 (1980): 329-35 [10] Ko, Tse-Hao. "The Effect of Pyrolysis on the Mechanical Properties and Microstructure of Carbon Fiber-Reinforced and Stabilized Fiber-Reinforced Phenolic Resins for Carbon/Carbon Composites." Polymer composites 14 (1993): 247-56 [11] Manocha, L. M., H. Bhatt and S. M. Manocha. "Development of Carbon/Carbon Composites by Co-Carbonization of Phenolic Resin and Oxidised Pan Fibers." Carbon 34 (1996): 841-49 [12] [13] [14] [15] [16] [17] [18] [19] [20] [21] [22] [23] [24] [25] Dhami, T. L., O. P. Bahl and P. K. Jain. "Carbon-Carbon Composites Made with Oxidised Pan (Panex) Fibers." Carbon 33 (1995): 1517-24 Fitzer, E., K. H. Geigl and W. Hüttner. "The Influence of Carbon Fibre Surface Treatment on the Mechanical Properties of Carbon/Carbon Composites." Carbon 18 (1980): 265-70 Manocha, Lalit M., Eiichi Yasuda, Yasuhiro Tanabe and Shiushichi Kimura. "Effect of Carbon Fiber Surface-Treatment on Mechanical Properties of C/C Composites." Carbon 26 (1988): 333-37 Beck, William M., Christopher J. Altamuro, Michael J. Chauby, Matthew S. Schwenger, Giuseppe R. Palmese, Joseph F. Stanzione III and James A. Newell. "Comperative Analysis of Kevlar, Pbo and Derived Carbon Fibers." SAMPE Technical Conference Proceedings Seattle, WA, April 18, 2023, Society for the Advancement of Material and Process Engineering. pp. 7. Newell, James A., D. K. Rogers, D. D. Edie and C. C. Fain. "Direct Carbonization of Pbo Fiber." Carbon 32 (1994): 651-58 Newell, James A., Dan D. Edie and E. Loren Fuller Jr. "Kinetics of Carbonization and Graphitization of Pbo Fiber." Journal of applied polymer science 60 (1996): 825-32 Kaburagi, Yutaka, Kenji Yokoi, Akira Yoshida and Yoshihiro Hishiyama. "Highly Graphitized Carbon Fiber Prepared from Poly (P-Phenylene-Benzo-Bis-Oxazole) Fiber." TANSO 2005 (2005): 111-14 Yu, Mengwen. "Structure-Processing-Property Relationships of Furanyl Benzoxazine Polymers Derived from Bio-Based Feedstocks." Ph.D., Drexel University, 2022 ASTM C373 − 18, “Standard Test Methods for Determination of Water Absorption and Associated Properties by Vacuum Method for Pressed Ceramic Tiles and Glass Tiles and Boil Method for Extruded Ceramic Tiles and Non-Tile Fired Ceramic Whiteware Products”, 2018, 10.1520/C0373-18: 10.1520/C0373-18, www.astm.org. ASTM D8132/D8132M − 17, “Standard Test Method for Determination of Prepreg Impregnation by Permeability Measurement”, 2017, 10.1520/D8132_D8132M-17: 10.1520/D8132_D8132M-17, www.astm.org. Rellick, Gerald. "Densification Efficiency of Carbon-Carbon Composites." Carbon 28 (1990): 589-94 Klucakova, M. "Rheological Properties of Phenolic Resin as a Liquid Matrix Precursor for Impregnation of Carbon–Carbon Composites with Respect to Conditions of the Densification Process." Composites Science and Technology 64 (2004): 1041-47 Muhammed, Faheem, Laure Moretti, Tania Lavaggi, Christopher Lam, Tao Tao, Suresh Advani and John W. Gillespie. "Influence of Pyrolytic Decomposition on the Microstructure Evolution of Benzoxazine-Derived Carbon–Carbon Composites." Journal of Materials Science 57 (2022): 21915-34 Lavaggi, Tania, Faheem Muhammed, Laure Moretti, John W. Gillespie and Suresh G. Advani. "Correlation of the Permeability and Porosity Development of Carbon/Carbon Composites during Pyrolysis." Composites Part A: Applied Science and Manufacturing 181 (2024) [26] Muhammed, Faheem, Tania Lavaggi, Suresh Advani and John W. Gillespie Jr. "Relating the Microstructural and Glass Transition Temperature Evolution of a Carbon–Carbon Composite Precursor during Pyrolysis Using Thermomechanical Analysis." Journal of applied polymer science 140 (2023)

Conference: SAMPE 2026

Publication Date: 2026/04/27

SKU: 84

Pages: 10

Price: $20.00